PROCESSING OF MATERIALS IN THE PROCESSES:
- cuts
- punching, bending
- lamination
- shaping
- sewing
- cellular rubber is used for water, wind and oil seals.
- due to its plastic properties (it is soft), cellular rubber is also used for thermal insulation and sound absorption
- Wainvest Europe offers cellular rubber with properties matched to the requirements of its application at the customer's site
EPDM caoutchouc (ethylene propylene diene monomer rubber)
- closed cells
- used for water and windproof seals
- weight: 120-140 kg / m³
- temperature range: Min -40ºC Max + 100ºC depending on the quality
- flammability class: FMVSS 302
EPDM caoutchouc white (ethylene propylene diene monomer rubber)
- closed cells
- used for water and windproof seals
- weight: 120 kg / m³
- temperature range: Min -30ºC Max + 75ºC depending on the quality
- flammability class: FMVSS 302
EPDM caoutchouc gray (ethylene propylene diene monomer rubber)
- closed cells
- used for water and windproof seals
- weight: 120 kg / m³
- temperature range: Min -30ºC Max + 75ºC depending on the quality
- flammability class: FMVSS 302
NITTO 685 EPDM caoutchouc (ethylene propylene diene monomer rubber)
- soft rubber with partially closed cells
- used for sealing, good sound absorption properties
- weight: 130 kg / m³
- temperature range: Min -40ºC Max + 135ºC (180ºC)
- flammability class: FMVSS 302
NITTO 1000 EPDM caoutchouc (ethylene propylene diene monomer rubber)
- soft rubber with partially closed cells
- used for sealing, good sound absorption properties
- weight: 95 kg / m³
- temperature range: Min -40ºC Max + 135ºC (180ºC)
- flammability class: FMVSS 302
NITTO 1200N EPDM caoutchouc (ethylene propylene diene monomer rubber)
- soft rubber with partially closed cells
- when compressed by 70%, very good sealing properties of water, air, dirt and dust, heat. Good sound absorption properties
- Low emission standard: DIN 75201, VDA 270,275 and 277. UV resistant
- thickness: 5-30mm
- weight: 95 kg / m³
- temperature range: Min -40ºC Max + 135ºC (180ºC)
- flammability class: FMVSS 302 (10mm) <100 mm / min
NITTO 6800 EPDM caoutchouc (ethylene propylene diene monomer rubber)
- closed-cell rubber
- very good water-sealing properties
- weight: 110 kg / m³
- temperature range: Min -40ºC Max + 135ºC (180ºC)
- flammability class: FMVSS 302
anti-condensation rubber
- closed-cell rubber
- anti-condensation protection for the protection of pipes, ventilation ducts, engine compartments
- high vapor permeability, low thermal conductivity
- weight: 110 kg / m³
- temperature range: Min -50ºC Max + 110ºC
- flammability class of coverings and sheets: B-s3, d0, UL approved V-0
NEOPRENE (CR) chloroprene rubber
- closed-cell rubber
- water, air and oil seals
- weight: 170-250 kg / m³
- temperature range: Min -40ºC Max + 100ºC
- flammability class: UL94 HF> 2mm
NBR Nitrile - acrylonitrile-butadiene rubber
- closed-cell rubber
- gaskets for diesel, petrol and oil seals
- weight: 200 kg / m³
- temperature range: -40º + 100º
- flammability class: UL94 HF
SI Silicone
- closed-cell rubber
- good thermal properties and electrical insulation.
- Weight: 250 kg / m³
- Temperature range: -80º + 200º (+ 260º)
- flammability class: FMVSS302
PVC polyvinyl chloride
- good at low temperatures -50 + 70 °
- used for sealing. Weight: 105-120 kg / m³
- cellular polyethylene is used for condensation sealing and insulation
- in laminates, cellular polyethylene is most often used as a base layer due to its thermal insulation, anti-moisture and sensory properties (thanks to it the surface is softer)
Cellular polyethylene
- sealing and condensation insulation
- chemically cross-linked
- weight: 28-150 kg / m³
- temperature range: Min. -40ºC Max. + 100ºC
- fire class: FMVSS302
PE 50
- closed cells
- physically cross-linked
- field of application: Packaging and shock absorption
- weight: 50 kg / m³
- temperature range: Min. -30ºC Max. + 70ºC
Alveolit
- closed cells
- sealing and insulation for heating / cooling
- weight: 25-185 kg / m³
- temperature range: Min. -40ºC Max. + 100ºC
- fire class: FMVSS 302
Alveosoft
- application: construction, windows
- hermetic, semi-closed cells
- temperature range: max. + 90ºC
- fire class: FMVSS 302
Plastazote LD
- sealing and condensation insulation
- physically cross-linked
- weight: 15-45 kg / m³
- temperature range: Min -70ºC Max + 95ºC
- fire class: FMVSS302
Evazote EV
- sealing and condensation insulation
- physically cross-linked
- weight: 30-45 kg / m³
- temperature range: Min -70ºC Max. + 65ºC
- fire class: FMVSS302
cellular polyether and cellular polyester
Wainvest Europe offers wide selection of the right material depends on the requirements of the customer's application. The materials from this group are used for various purposes, including slut absorption, sealing, air filtration, air filtration but also as a base layer for laminate due to its sensory properties.
lamilex
- semi-closed cell polyether.
- suitable for sound absorption
- weight: 27-30 kg / m³
- fire class: FMVSS 302
fireflex
- open-celled cellular polyester
- sound absorption
- high fire resistance
- weight: 30 kg / m³
- fire class: UL-94 HF-1, FMVSS302
isoseal / situseal
- closed-cell or open-cell cellular polyether
- sealing and sound absorption
- weight: 40 kg / m³
- temperature range: Min. -40ºC Max. + 120ºC
- fire class: FMVSS 302> 13mm
superseal
- semi-open cell polyester superseal cells
- often used for automotive sealing
- weight: 60 kg / m³ or 45 kg / m³
- fire class: FMVSS302
recyling foam (bonded foam)
- recycled cellular polyether
- weight: 100-160 kg / m³
- good sound absorption
- temperature range: Min -40ºC Max + 120ºC
- fire class: FMVSS 302
basotect
- melamine foam,
- lightweight sound absorber
- open cells
- weight: 9 kg / m³
- temperature range: max. + 240ºC
- fire class: FMVSS302, UL94 V-0
bulpren
- cellular polyester with open cells
- filtering material of air filters, for the loudspeaker cover
- weight: 30 kg / m³
- offered in 10-20-30 PPI
flame resistant filter
- cellular polyester
- impregnated with good fire protection properties.
- the filter confirms
- weight: 50 kg / m³
- fire class: UL94 V-0
- offered in 20-30 PPI
fabric/textile on foam
- fabric/textile laminated on foam
- selection of fabrics and textiles according to the customer's needs
- interesting sensory effect (aesthetic surface pleasant to the touch and soft at the same time)
PVC film on foam
- perforated PVC film laminated on the foam
- aesthetic surface finish
aluminum foil on foam
- aluminum foil laminated on the foam
- protective function and washable surface
polyurethane foil on foam
- laminated polyurethane film on the foam
- sealing function
- prevents dust from getting inside the foam structure
Layers are used for loading vehicles that fall within the scope of material sounds, e.g. in vehicles and household appliances. For this purpose, I remove weight and structure on the surface of sheets and plastics.
damping pad 1.2 kg
- reduction of vibrations and structured material sounds
- self-adhesive
- thickness: 1.3 mm
- weight: 1.2 kg / m²
damping pad 1.7 kg
- reduction of vibrations and structured material sounds
- self-adhesive
- thickness: 1.7 mm
- weight: 1.7 kg / m²
damping pad 2.6 kg
- reduction of vibrations and structured material sounds
- self-adhesive
- thickness: 2.6 mm
- weight: 2.6 kg / m²
damping pad 1.3-2 kg
- reduction of vibrations and structured material sounds
- self-adhesive
- thickness: 1.4-2.1 mm
- weight: 1.3-2 kg / m²
damping pad with aluminum
- reduction of vibrations and structured material sounds
- fire-resistant and washable aluminum surface
- thickness: 1.4-2.1 mm
- weight: 1.3-2 kg / m²
heavy layer bitumen
- sound reduction
- weight: 3-10 kg / m²
- temperature range: Min -20ºC Max. + 80ºC
- fire class: UL94 V-2
heavy layer 3.5 kg
- sound reduction
- self-adhesive or not
- weight: 3.5 kg / m²
- temperature range: Min -30ºC Max + 75ºC
- fire class: FMVSS 302
heavy layer 5 kg
- sound reduction
- self-adhesive or not
- weight: 5 kg / m²
- temperature range: Min -30ºC Max + 75ºC
- fire class: UL94 V-0, FMVSS 302
heavy layer 6.5-7 kg
- sound reduction
- self-adhesive or not
- weight: 6.5-7 kg / m²
- temperature range: Min -30ºC Max + 130ºC (+ 160ºC)
- fire class: FMVSS 302
Polyester fiber and textiles made of various blends of fibrous components.
The choice of material from a wide range of fibrous and felt materials depends on the needs of the customer's application. Felt with one of the ingredients are recycled textile fibers are often used in the automotive industry due to their sound-absorbing properties and low price.
polyester fibre felt
- good sound absorption properties
- ecological due to the fact that it is made of, among others, textile waste
- contains polyester fibre
- can be laminated with other materials or with tape
- weight: 100-3000 g / m²
- thickness: 5-80mm
- fire class: FMVSS302
polyester fibre felt white
- good sound absorption properties
- ecological due to the fact that it is made of, among others, textile waste
- contains polyester fibers
- can be laminated with other materials or with tape
- weight: 100-4000g / m²
- thickness: 5-80mm
- fire class: FMVSS 302 / EN13501-1, B-s1, d0
polyester fibre felt black
- good sound absorption properties
- ecological due to the fact that it is made of, among others, textile waste
- contains polyester fibers
- can be laminated with other materials or with tape
- weight: 100-4000g / m²
- thickness: 5-80mm
- fire class: FMVSS 302 / EN13501-1, B-s1, d0
polyester fibre felt gray
- good sound absorption properties
- ecological due to the fact that it is made of, among others, textile waste
- contains polyester fibers
- can be laminated with other materials or with tape
- weight: 100-4000g / m²
- thickness: 5-80mm
- fire class: FMVSS 302 / EN13501-1, B-s1, d0
polyester fibre felt blend
- good sound absorption properties
- ecological due to the fact that it is made of, among others, textile waste
- contains polyester fibers
- can be laminated with other materials or with tape
- weight: 100-3000g / m²
- thickness: 5-80mm
- fire class: FMVSS302
needle-punched polyester
- the materials do not squeak
- it is possible to combine sheets with a goal
- weight: 100-2500g / m²
- thickness: 5-30mm
- fire class: FMVSS 302 / EN13501-1, B-s1, d0
flame resistant polyester fibers
- good sound absorption properties
- made of fire retardant fibers
- weight: 100-3000g / m²
- thickness: 5-80mm
- fire class: on request
echofelt
- made of conp and polyester needle service
- good strange-absorbing properties
- can be laminated with other materials or with tape
- weight: 300-1400g / m² ± 10%
- thickness: 3-20 mm ± 2 mm
Thinsulate
- by trapping air in the layer, it thermally insulates and removes moisture
- low cutting weight of fine fibers
felt from recycled fabrics
- ecological used in the automotive industry
- good sound absorption property
- weight: 500-2400 g / m²
- thickness: 8-37 mm
- fire class: FMVSS 302
airfelt
- ecological
- made of, inter alia, polyester fiber, made of PET bottles processing
- basis weight: 100-4000g / m²
- thickness: 5-80mm
- fire class: EN13501-1, B-s1, d0
Non-woven polyester
- protection against squeaking
- color: gray, black and white in various weights (g / m²)
Laminated polyester
- lamination of textiles on fibrous materials
Wainvest Europe selects and offers materials that are properly selected to meet the requirements of their use at the customer. A wide selection of CR (neoprene), EPDM, NBR, NR, SI (silicone) and SBR allows us to offer a rubber depending on the needs related to the influence of cold and heat on the material, with ozone resistance, oil resistance, durability and material aging . The available formats are sheet, tube and profiles.
mixed-cell polyurethane (PUR)
- good damping and elastic properties
- high flexibility and durability
EPDM 50º
- resistant to aging of the material and chemicals
- ozone resistant
- hardness: 50-70 ° Sh A
EPDM 60º
- resistant to aging of the material and chemicals
- ozone resistant - hardness: 50-70 ° Sh A
EPDM 70º
- resistant to aging of the material and chemicals
- ozone resistant - hardness: 50-70 ° Sh A
EPDM 60º white
- resistant to aging of the material and chemicals
- ozone resistant
- good electrical insulation properties
- hardness: 60 ° Sh
SBR (styrene butadiene rubber)
- good durability.
- hardness: 50-70 ° Sh A
CR Cloroprene Rubber (neoprene)
- resistant to ozone and aging,
- limited resistance to oils
- hardness: 50-70 ° Sh A
NBR (nitrile butadien rubber)
- Good oil resistance
- Hardness: 50-70 ° Sh
NR natural rubber
- good durability.
- hardness 40 ° Sh A
SI (silicone)
- retains good quality when exposed to cold and heat
- temperature range: from -70 ° C to + 200 ° C.
- colors: red, white and transparent.
- hardness: 60 ° Sh A
mats
Wainvest Europe offers mats with mats in various structures, thicknesses and colors. Sealing (gaskets), protective (machine and process), safety (electrical, fire / smoke insulation) and floor mats (industrial mats).
Different types of mat materials can be used in many ways, for example as carpet for shelves, walls or floors, as mats in elevators, trucks and in various industrial work areas
narrow grooves pattern
- thickness: 3mm
- colors: black and gray
medium grooves pattern
- thickness: 3.5 mm
- colors: black and gray
wide grooves pattern
- thickness: 3.5 mm
- colors: black and gray
carpet flooring
- thickness: 2mm
- color: standard dark gray, other colors on request
- available with a self-adhesive surface
diamond pattern
- thickness: 3mm and 5mm
- colors: black and gray
circle pattern
- thickness: 3mm
- colors: black and gray
Wainvest Europe offers plastic with high durability. A wide range of plastics have a combination of mutual properties with good properties in terms of high quality and properties on the range.
Poliproypen (PP)
- one of the most popular thermoplastic materials.
- the material contains propene and has good fatigue resistance.
- thickness: 1-3 mm
ABS acrylonitrile butadiene styrene
- good low temperature properties
- styrene-based copolymer
- thickness range 1-4 mm
- different surface structure similar to leather (grain) possible
polyester mylar film
- thin, durable material, suitable for electrical insulation, as well as resistant surfaces on other materials
- good material for friction-reducing washers or seals in combination with bolted connections.
- thickness range 0.12-0.35mm
polyurethane protective film
- used to protect, for example, painted surfaces
- 0.3 mm thick, transparent
Wainvest Europe offers wood material for a variety of constructions. Plywood, fibreboard, cardboard formed into furniture elements.
fiberboard
- made of 75% recycled paper (FSC) and 25% long-grain kraft paper
- used for molded furniture components
- thickness: 1.00 - 1.25 - 1.4 - 1.6 - 2 - 3 mm
- weight: 0.9 kg / dm3
FSC fibreboard
- FSC recycled fibreboard
- mainly used for sofas and armchairs
- thickness: 1.85 - 3.2 mm
- weight: 0.9 kg / dm3
FSC high-density fibreboard
- made of recycled paper up to 75% (FSC) and 25% kraft paper with long fibers (FSC)
- mainly used for compression molding of harder products such as truck seats
- thickness: 1.4 - 1.6 mm
- weight: 1.1 kg / dm3
varnished fiberboard
- made of recycled paper
- used for boxes, folders and other products.
- thickness: as required
- weight: 0.9 kg / dm3
plywood
- used for furniture elements
- we have most thicknesses, mainly birch plywood.
- qualities: B / BB, BB / BB, BB / CP, CP / CP, C / C
- thickness: 1.5-12mm
threaded tee nut in wood material
- M4-M10 are delivered in combination with plywood and fibreboard
- T-nut installed
- positioning precision thanks to the robot's work
masonite plate
- mainly used as packaging, but also for sofas and armchairs.
- thickness: 3-4.8mm